1. The uneven thickness of the spiral wall is caused by the uneven rolling centerline of the piercing machine, the unequal inclination of the two rolls, or the excessive reduction of the front head. The uneven wall thickness is generally along the full length of the steel pipe. Spiral distribution. During the rolling process, the uneven wall thickness caused by the premature opening of the centering roller, improper adjustment of the centering roller, and the jitter of the ejector rod are generally distributed in a spiral shape along the entire length of the steel pipe.
Measures: Adjust the rolling centerline of the piercing machine to make the inclination angles of the two rolls equal, and adjust the tube mill according to the parameters given in the rolling table. In response to this situation, adjust the opening time of the centering roller according to the capillary exit speed. Do not open the centering roller too early during the rolling process to prevent the ejector rod from shaking and causing uneven wall thickness. The opening degree of the centering roller needs to be adjusted appropriately according to the change of capillary diameter, and the amount of capillary beating is considered.
2. Causes of uneven linear wall thickness: improper adjustment of the height of the core rod pre-piercing saddle, the mandrel pre-pierces the capillary tube on a certain surface, causing the capillary tube to drop too quickly on the contact surface, resulting in uneven wall thickness or even Pull dent defect. The tandem roll gap is too small or too large. Deviation of the centerline of the tube mill. The uneven reduction of single and double frames will cause linear symmetry deviations in the direction of the single-frame (extra-thickness) and the direction of the double frame (extra-thickness). The fracture of the mortar and the large gap between the inner and outer rolls will cause the linear asymmetric deviation of the steel pipe. Improper adjustment of continuous rolling, stacking, drawing, and rolling will cause uneven linear wall thickness.
Measures: Adjust the height of the core rod pre-piercing saddle to ensure that the core rod and the capillary are aligned. When changing the pass and rolling specifications, measure the roll gap to keep the actual roll gap consistent with the rolling table. Adjust the rolling centerline with an optical centering device, and correct the centerline of the tube mill during annual overhauls. Change the broken mortar frame in time, and implement the measurement of the inner and outer gap of the continuous roll. If there is a problem, change it in time. During continuous rolling, steel drawing and pile-up should be avoided.
3. Causes of uneven wall thickness at the head and tail: the cutting slope at the front end of the tube blank, excessive bending, and incorrect centering holes of the tube blank can easily cause uneven wall thickness of the tube head. During piercing, the elongation coefficient is too large, the roll speed is too high, and the rolling is unstable. The unstable steel throwing of the piercer can easily cause uneven wall thickness at the tail of the capillary.
Measures: Check the tube blank to prevent the front end of the tube blank from cutting slope and large reduction. The centering hole should be corrected when changing the hole type or overhauling. Use lower piercing speed to ensure rolling stability and uniformity of capillary wall thickness. When the roll speed is adjusted, the matched guide plate is also adjusted accordingly. Pay attention to the use status of the guide plate and increase the inspection of the guide plate bolts, reduce the movement range of the guide plate during steel rolling, and ensure the stability of steel throwing. Vietnam spent more than four billion U.S. dollars importing roughly 6.8
Threeway Steel is known as a professional supplier engaged in manufacturing and distributing a wide range of steel pipe, and our headquarter located the central part of China – Hunan and six associated factories throughout China.
Threeway Steel is known as a professional supplier engaged in designing, manufacturing and distribution of a wide range of steel products with the headquarter located the central part of China – Hunan and six associated factories throughout China.
Threeway Steel is known as a professional supplier engaged in designing, manufacturing and distribution of a wide range of steel products with the headquarter located the central part of China – Hunan and six associated factories throughout China.
Threeway Steel is known as a professional supplier engaged in designing, manufacturing and distribution of a wide range of steel products with the headquarter located the central part of China – Hunan and six associated factories throughout China.
Threeway Steel is known as a professional supplier engaged in designing, manufacturing and distribution of a wide range of steel products with the headquarter located the central part of China – Hunan and six associated factories throughout China.